Stainless Steel Pipe
201 Stainless Steel Pipe
201 stainless steel generally refers to 201 stainless steel and acid resistant steel. 201 stainless steel refers to the steel that is resistant to the corrosion of weak media such as atmosphere, steam and water, while acid resistant steel refers to the steel that is resistant to the corrosion of chemical corrosive media such as acid, alkali and salt.
201 stainless steel is composed primarily of iron with between 16 and 18% chromium and up to 0.15% carbon. It also contains small amounts of manganese, nickel, silicon, nitrogen, and copper. It has higher formability than the 300 series grades. In addition, it can be hardened by cold working processes but not heat-treated like 304 or 316 grades. 201 is a high manganese and low nickel stainless steel with low nickel content and poor corrosion resistance. It is widely used in various tabletops, countertops, kitchenware, outdoor decoration engineering, urban decoration industry and low-grade household products. It is also used in medical instruments and automotive parts that require flexibility while maintaining strength under pressure.
Product Parameters
| Product Name | 201 Stainless Steel Pipe |
|---|---|
| Type | Steel Pipe |
| Outer Diameter (Round Tube) | 4mm - 200mm |
| Outer Diameter (Square Tube) | 10×10mm - 100×100mm |
| Outer Diameter (Rectangular Tube) | 10×20mm - 50×100mm |
| Wall Thickness | 0.6mm - 6.0mm |
| Length | 1 - 6 meters (customizable) |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. |
| Surface | Black, Bright Polished, Rough Turning, Matt Surface Treatment, No.4, BA, etc. |
| Scope of Application | Food processing, textile operations, breweries, water treatment plants, oil & gas processing, fertilizers and pesticides, chemical applications, construction, pharmaceuticals, auto parts, etc. |
| Certificate | ISO, SGS, BV, etc. |
| Production Technology | Hot Rolling, Cold Rolling |
| Edge Processing | Edging, Trimming |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
|---|---|---|---|---|---|---|
| ≤ 0.03 | ≤ 1.0 | ≤ 2.0 | 18.0 – 20.0 | 8.0 – 12.0 | ≤ 0.03 | ≤ 0.035 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
|---|---|---|---|
| ≥ 520 | ≥ 205 | ≥ 40 | ≤187HB / ≤90HRB / ≤200HV |
Physical Performance
| Density (g/cm³) | Modulus of Elasticity (GPa) | Thermal Expansion (10⁻⁶/°C) | Thermal Conductivity (W/m·K) | Resistivity (μΩ·cm) |
|---|---|---|---|---|
| 8.03 | 193 | 16.9 | 16.2 | 72 |