Stainless Steel Bar
405 Stainless Steel Bar
405 stainless steel is categorized as austenitic stainless steel material that is resistant to corrosion with good mechanical properties. The bars are usually used as manufacturing parts in marine engineering, petrochemical industry, food processing and other fields.
405 stainless steel bar is made of a high-alloy stainless steel material primarily consisting of chromium, nickel and copper. It can perform well in strong acid environments such as oxidizing acid, nitric acid, and sulfuric acid. So the bars can be used in various corrosive environments, such as marine environment, chemical media, etc. Besides, 405 stainless steel comes with good strength and toughness and can withstand substantial pressure and impact. At the same time, the bars can be used for cutting, bending, welding and other operations with the outstanding mechanical properties. Lastly 405 stainless steel bars are highly advantageous in some applications requiring high temperature processing for their incredible heat resistance nature.
Product Parameters
| Product Name | 405 Stainless Steel Bar |
|---|---|
| Type | Steel Bar |
| Outer Diameter (Round Bar) | 4mm - 500mm |
| Outer Diameter (Hexagon Bar) | 18mm - 57mm (11/16″ to 2-3/4″) |
| Outer Diameter (Square Bar) | 18mm - 47mm (11/16″ to 1-3/4″) |
| Flat Steel | 1/2″ to 10″, Thickness: 2mm - 150mm (customizable) |
| Length | 1 - 6 meters (customizable) |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. |
| Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No.4, BA, etc. |
| Scope of Application | Shipbuilding, defense, automotive, textiles, paper and pulp, manufacturing, cement, heavy earthmoving equipment and construction, etc. |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P | Mo |
|---|---|---|---|---|---|---|---|
| ≤ 0.03 | ≤ 1.0 | ≤ 2.0 | 16.0 – 18.0 | 10.0 – 14.0 | ≤ 0.03 | ≤ 0.045 | 2.0 – 3.0 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
|---|---|---|---|
| ≥ 480 | ≥ 177 | ≥ 40 | ≤187HB / ≤90HRB / ≤200HV |
Physical Performance
| Density (g/cm³) | Modulus of Elasticity (GPa) | Thermal Expansion (10⁻⁶/°C) | Thermal Conductivity (W/m·K) | Resistivity (μΩ·cm) |
|---|---|---|---|---|
| 7.99 | 193 | 16.0 | 16.2 | 74 |