Stainless Steel Pipe
310S Stainless Steel Pipe
310S stainless steel is austenitic chromium-nickel stainless steel, with good oxidation resistance, corrosion resistance, because of a higher percentage of chromium and nickel, it has better creep strength, can work at high temperatures continuously, with good high temperature resistance.
310S stainless steel pipe has good oxidation resistance, corrosion resistance, acid and alkali resistance given its high content of nickel (Ni) and chromium (Cr). The strength is improved due to its solid solution strengthening effect after adding the content of carbon in austenitic stainless steel,. The chemical composition characteristics of austenitic stainless steel are based on chromium and nickel to add molybdenum, tungsten, niobium and titanium, and because of its face-centered cubic structure, it has high strength and creep strength at high temperatures. 310S stainless steel is often used in the manufacture of boiler, steam turbine, industrial furnace and aviation, petrochemical.
Product Parameters
| Product Name | 310S Stainless Steel Pipe |
|---|---|
| Type | Steel Pipe |
| Outer Diameter (Round Tube) | 4mm - 200mm |
| Outer Diameter (Square Tube) | 10×10mm - 100×100mm |
| Outer Diameter (Rectangular Tube) | 10×20mm - 50×100mm |
| Wall Thickness | 0.6mm - 6.0mm |
| Length | 1 - 6 meters (customizable) |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. |
| Surface | Black, Bright Polished, Rough Turning, Matt Surface Treatment, No.4, BA, etc. |
| Scope of Application | Food processing, textile operations, breweries, water treatment plants, oil & gas processing, fertilizers and pesticides, chemical applications, construction, pharmaceuticals, auto parts, etc. |
| Certificate | ISO, SGS, BV, etc. |
| Production Technology | Hot Rolling, Cold Rolling |
| Edge Processing | Edging, Trimming |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
|---|---|---|---|---|---|---|
| ≤ 0.03 | ≤ 1.0 | ≤ 2.0 | 18.0 – 20.0 | 8.0 – 12.0 | ≤ 0.03 | ≤ 0.035 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
|---|---|---|---|
| ≥ 520 | ≥ 205 | ≥ 40 | ≤187HB / ≤90HRB / ≤200HV |
Physical Performance
| Density (g/cm³) | Modulus of Elasticity (GPa) | Thermal Expansion (10⁻⁶/°C) | Thermal Conductivity (W/m·K) | Resistivity (μΩ·cm) |
|---|---|---|---|---|
| 8.03 | 193 | 16.9 | 16.2 | 72 |